Abstract
Initial experimental work at 700°–800 °C is in progress to develop a lifetime model for supercritical CO2 (sCO2) compatibility for a 30-year lifetime of a >700 °C concentrated solar power system. Nickel-based alloys 282, 740H and 625 and Fe-based alloy 25 are being evaluated in 500-h cycles at 1 and 300 bar, and 10-h cycles in 1 bar industrial grade CO2. The alloys showed similar low rates of oxidation in 1 and 300 bar CO2 in 500-h cycles at 750 °C. However, in 10-h cycles, alloy 25 showed accelerated attack at 700° and 750 °C. Transmission electron microscopy scale cross-sections on alloy 25 after 1000 h at 700 °C in sCO2 and in air only showed a small row of carbides beneath the scale in the former environment. Similar characterisation was performed on alloys 625 and 282 after sCO2 exposure at 750 °C.