Abstract
The mechanical properties of NBG-18 nuclear grade graphite have been characterized using small specimen test techniques and statistical treatment on the test results. New fracture strength and toughness test techniques were developed to use subsize cylindrical specimens with glued heads and to reuse their broken halves. Three sets of subsize cylindrical specimens with the different diameters of 4 mm, 8 mm, and 12 mm were tested to obtain tensile fracture strength. The longer piece of the broken halves was cracked from side surfaces and tested under three-point bend loading to obtain fracture toughness. Both the strength and fracture toughness data were analyzed using Weibull distribution models focusing on size effect. The mean fracture strength decreased from 22.9 MPa to 21.5 MPa as the diameter increased from 4 mm to 12 mm, and the mean strength of 15.9 mm diameter standard specimen, 20.9 MPa, was on the extended trend line. These fracture strength data indicate that in the given diameter range the size effect is not significant and much smaller than that predicted by the Weibull statistics-based model. Further, no noticeable size effect existed in the fracture toughness data, whose mean values were in a narrow range of 1.21 – 1.26 MPa. The Weibull moduli measured for fracture strength and fracture toughness datasets were around 10. It is therefore believed that the small or negligible size effect enables to use the subsize specimens and that the new fracture toughness test method to reuse the broken specimens to help minimize irradiation space and radioactive waste.