Abstract
Deployment of additively manufactured materials into nuclear energy systems requires investigation of the full range of the unique environmental effects on these materials. Hydrogen isotopes are common gaseous species in nuclear reactors and exhibit ample high mobility in most materials. While hydrogen isotopes mobility in wrought stainless steel is well understood, this property is not thoroughly studied for its additively manufactured variants. In this study, we investigated the deuterium permeation and retention in 316L stainless steel manufactured by laser powder bed fusion. The results showed that the deuterium permeability in the as-built additively manufactured 316L stainless steel (AM SS316L) is greater than that of the reference wrought 316L stainless steel by a factor of 2.8. However, the stress-relieved and solution-annealed AM SS316L samples exhibit lower deuterium permeability in comparison with the as-built condition. Following the solution annealing, the deuterium permeability of AM SS316L is comparable with that of the reference wrought SS316L. Deuterium retention in the as-built AM SS316L is 45% higher than that of the wrought 316L stainless steel and slightly higher than that of the two thermally annealed AM SS316L materials. Transmission electron microscopy and positron annihilation lifetime spectroscopy were used to obtain microstructural information used to determine deuterium permeation and retention behavior in the studied materials.