Density Measurements of Molten LiF–BeF2 and LiF–BeF2–LaF3 Salt Mixtures by Neutron Radiography

Publication Type
Journal
Journal Name
ACS Omega
Publication Date
Volume
6

The densities of eutectic (LiF)2–BeF2 and mixtures of this salt (FLiBe) with LaF3 were measured by dilatometry and by neutron attenuation from 673 K to 1,073 K. Because LaF3 has a limited solubility in FLiBe, it was necessary to determine the amount of LaF3 in solution before the density could be determined. The FLiBe density determination was favorably benchmarked against the literature data. A simple comparison was not available for the LaF3–FLiBe mixtures, so extrapolation of published data was necessary based on analysis using the Molten Salt Thermal Properties Database-Thermochemistry, or MSTDB-TC, developed by the US Department of Energy. Solubilities for LaF3 in FLiBe ranged from 1 to 4 mol % over 673 to 1,073 K. The salt system was heated and cooled over 24 h to evaluate potential changes in composition and hysteresis during the measurement. Changes in the meniscus were observed, and these were included in the correction for density determinations. Salt surface tension may have led to supersaturation of LaF3 in the salt because the solubility curve was nonlinear with respect to the inverse temperature, as would be expected for an ideal system. Surface tension measurements are currently underway to test this hypothesis.