Abstract
Understating effects of the number, type and concentration of alloying elements in single-phase concentred solid-solution alloys (SP-CSAs) on defect dynamics and microstructure evolution is pivotal for developing next-generation radiation-tolerant structural alloys. A specially chosen set of SP-CSAs with different type and number of alloying elements (Ni80Fe20, Ni80Cr20 and Ni40Fe40Cr20) are investigated using 1.5 MeV Mn ions over a wide fluence range, from 2×1013 to 1×1016 ions cm-2, at room temperature. Based on a combination of Rutherford backscattering spectroscopy in channeling geometry and molecular dynamics simulations, the results demonstrate that Ni40Fe40Cr20 is more irradiation-resistant than Ni80Fe20, Ni80Cr20 and elemental Ni in the low fluence regime. While chemical complexity of this set of SP-CSAs is clearly demonstrated to affect defect evolution through suppressed defect production and enhanced recombination at early stages, the effect of the mixed ferro- and anti-ferromagnetic interactions is not the only controlling factor responsible for the improved radiation performance. The observed strong alloying effect on defect evolution is attributed to the altered defect migration mobility of defect clusters in these alloys, an intrinsic characteristic of the complex energy landscapes in CSAs.