Abstract
Thin film Cu-Ni alloys ranging from 2-8nm were synthesized and their optical properties were measured as-deposited and after a laser treatment which dewet the films into arrays of spatially correlated nanoparticles. The resultant nanoparticle size and spacing are attributed to laser induced spinodal dewetting process. The evolution of the spinodal dewetting process is investigated as a function of the thin film composition which ultimately dictates the size distribution and spacing of the nanoparticles. The optical measurements of the copper rich alloy nanoparticles reveal a signature absorption peak suggestive of a plasmonic peak which red-shifts with increasing nanoparticle size and blue shifts and dampens with increasing nickel concentration.