Publication Type
Journal
Journal Name
Scripta Materialia
Publication Date
Page Numbers
94 to 98
Volume
162
Issue
1
Abstract
Oxide dispersion strengthened (ODS) FeCrAl alloy (Fe-12Cr-5Al wt%) was neutron irradiated to 1.8 displacements per atom (dpa) at 215, 357, and 557 °C to investigate (Y,Al,O) nano-oxide stability and Cr-rich α′ precipitate formation using atom probe tomography. The nano-oxide sizes remain unchanged after irradiation, but the compositions are dependent on irradiation temperature due to competition between ballistic dissolution and precipitate reformation. Cr-rich clusters observed after 357 °C irradiation have lower Cr contents (61 at.%) than equilibrium α′, with a lower number density than wrought FeCrAl alloys. This suggests a suppression of α′ precipitation due to the high sink strength of ODS FeCrAl.
